Oil and Gas Application Corrosion Resistant Inconel 600 Round Bars
DINGSCO dedicated to providing our customers with best quality products, fastest possible deliveries, most competitive prices of Nickel Based Corrosion Resistant and High Temperature alloys in bars,rods,forged flanges, valve parts, forged shapes (shafts, discs, blocks, hubs,rings, cylinders and other custom shapes) according to ASTM,ASME,API,AMS, NACE and other industry standards.
Common Trade Names:
- Alloy 600, Inconel® 600, Nickel 600
Specifications:
UNS: N06600
W. NR.: 2.4816
Features:
- Virtually immune to chloride ion stress corrosion cracking
- Good caustic corrosion resistance
- Resistant to dry Cl2 to about 1000°F
- Oxidation resistance to 2000°F
- Carburization resistance
Proformance Profile:
Inconel® 600 is a nickel-base alloy with excellent carburization, and good oxidation resistance at elevated temperatures. The alloy has long been used in the heat treating industry for many of the same applications as RA330®. 600 alloy has useful resistance to dry Cl2 and HCl gases at moderately elevated temperatures. Alloy 600 is not suggested for use at red heat when sulfur is present due to elevated nickel quantities.
Grades 200 and 201 nickel are normally preferred for handling concentrated, high temperature caustic. However, when sulfur compounds are present as well, or for ammonium hydroxide service, 600 alloy is suggested. 600 alloy is subject to stress corrosion cracking in hot, concentrated caustic alkalies. To avoid stress corrosion cracking, the 600 alloy fabrication should be fully stress relieved prior to use. A minimum treatment of 1650°F for 1 hour is suggested, but 1800-1850°F for 1 hour preferred.
Applications:
- Heat treating muffles and retorts
- Vacuum furnace fixtures
- Chlorination equipment to 1000°F
- Titanium dioxide plants
| Grade | UNS | Density (g/cm3) | Tensile Strength (MPa min) | Yield Strength (MPa min) | Reduction of Area min (%) | Elongation min (%) | Hardness (HRC) |
| INCONEL 600 | N06600 | 8.47 | 552MPa min | 241MPa min | / | 30% min | / |
Chemical Composition(%):
| Ni | Cr | Fe | C | Mn | S | Si | Cu |
| 72.0min | 14.0-17.0 | 6.0-10.0 | 0.15max | 1.0max | 0.015max | 0.5max | 0.5max |